HAYNES® Waspaloy alloy

HAYNES® Waspaloy alloy  is an age-hardenable, nickel-based superalloy that possesses excellent strength at elevated temperatures.

 

Chemical composition

Composition

UNS N07001
%

Nickel Balance
Cobalt 12.00 - 15.00
Chromium 18.00 - 21.00
Molybdenum 3.50 - 5.00
Iron 2.00 max
Aluminum 1.20 - 1.60
Titanium 2.75 - 3.25
Carbon 0.03 - 0.10
Manganese 1.00 max
Silicon 0.75 max
Boron 0.003 - 0.01
Copper 0.50 max
Phosphorous 0.030 max
Sulfur 0.030 max
Zirconium 0.02 - 0.12

 

Physical properties

  Metric English
Density 8.20 g/cm³ 0.296 lbs/in³
Modulus of Elasticity 213 GPa 30.9 Mpsi
Electrical resistivity 1,240 µohm*mm 49 µohm*in
Thermal Conductivity 12.6 W/(m*°C) 88 BTU*in/(hr*ft²*°F)
Coefficient of thermal expansion 13.9 µm/(m*°C) 7.6 µin/(in*°F)

*Values calculated at 22 °C [72 °F]

 

Mechanical properties

Cold worked
%

Yield strength

Ultimate tensile strength

Elongation
%

0 586 MPa [85 ksi] 1027 MPa [149 ksi] 43
20 1089 MPa [158 ksi] 1262 MPa [183 ksi] 11
37 1434 MPa [208 ksi] 1731 MPa [251 ksi] 3

* Values are typical and may not represent all diameters. Test method will affect results.
All data represent results from a 25.4 cm [10 in] test gauge length.

 

HAYNES® Waspaloy alloy

HAYNES® Waspaloy alloy  is an age-hardenable, nickel-based superalloy that possesses excellent strength at elevated temperatures.

 

Chemical composition

Composition

UNS N07001
%

Nickel Balance
Cobalt 12.00 - 15.00
Chromium 18.00 - 21.00
Molybdenum 3.50 - 5.00
Iron 2.00 max
Aluminum 1.20 - 1.60
Titanium 2.75 - 3.25
Carbon 0.03 - 0.10
Manganese 1.00 max
Silicon 0.75 max
Boron 0.003 - 0.01
Copper 0.50 max
Phosphorous 0.030 max
Sulfur 0.030 max
Zirconium 0.02 - 0.12

 

Physical properties

  Metric English
Density 8.20 g/cm³ 0.296 lbs/in³
Modulus of Elasticity 213 GPa 30.9 Mpsi
Electrical resistivity 1,240 µohm*mm 49 µohm*in
Thermal Conductivity 12.6 W/(m*°C) 88 BTU*in/(hr*ft²*°F)
Coefficient of thermal expansion 13.9 µm/(m*°C) 7.6 µin/(in*°F)

*Values calculated at 22 °C [72 °F]

 

Mechanical properties

Cold worked
%

Yield strength

Ultimate tensile strength

Elongation
%

0 586 MPa [85 ksi] 1027 MPa [149 ksi] 43
20 1089 MPa [158 ksi] 1262 MPa [183 ksi] 11
37 1434 MPa [208 ksi] 1731 MPa [251 ksi] 3

* Values are typical and may not represent all diameters. Test method will affect results.
All data represent results from a 25.4 cm [10 in] test gauge length.